Thermodynamic and Kinetic Studies of the Precipitation of Double-Doped Amorphous Calcium Phosphate and Its Behaviour in Artificial Saliva.

Simulated body fluid (SBF) and artificial saliva (AS) are used in biomedical and dental research to mimic the physiological conditions of the human body. In this study, the biomimetic precipitation of double-doped amorphous calcium phosphate in SBF and AS are compared by thermodynamic modelling of chemical equilibrium in the SBF/AS-CaCl-MgCl-ZnCl-KHPO-HO and SBF/AS-CaCl-MgCl-ZnCl-KHPO-Glycine/Valine-HO systems. The saturation indices (SIs) of possible precipitate solid phases at pH 6.5, close to pH of AS, pH 7.5, close to pH of SBF, and pH 8.5, chosen by us based on our previous experimental data, were calculated. The results show possible precipitation of the same salts with almost equal SIs in the two biomimetic environments at the studied pHs. A decrease in the saturation indices of magnesium and zinc phosphates in the presence of glycine is a prerequisite for reducing their concentrations in the precipitates. Experimental studies confirmed the thermodynamic predictions. Only X-ray amorphous calcium phosphate with incorporated Mg (5.86-8.85 mol%) and Zn (0.71-2.84 mol%) was obtained in the experimental studies, irrespective of biomimetic media and synthesis route. Solid-state nuclear magnetic resonance (NMR) analysis showed that the synthesis route affects the degree of structural disorder of the precipitates. The lowest concentration of dopant ions was obtained in the presence of glycine. Further, the behaviour of the selected amorphous phase in artificial saliva was studied. The dynamic of Ca, Mg, and Zn ions between the solid and liquid phases was monitored. Both direct excitation P NMR spectra and H-P CP-MAS spectra proved the increase in the nanocrystalline hydroxyapatite phase upon increasing the incubation time in AS, which is more pronounced in samples with lower additives. The effect of the initial concentration of doped ions on the solid phase transformation was assessed by solid-state NMR.